ASTM A48 Class 35 Gray Cast Iron

Primary Designation:ASTM A48 Class 35

Aliases:

Class 35 Gray IronSAE G3500 Gray Iron

Mat Grades internal verification confirms source-backed fidelity and data integrity. It does not constitute external certification or guaranteed lot conformity. Read engineering disclaimer →

Compare Equivalents

Download PDF Download Excel

Report an issue

Data Completeness:6 composition elements and 9 condition-specific property values cataloged.

Omitted fields represent unverified properties. "Missing is better than invented."

Key Engineering Properties

Representative source rows, qualified by their reported conditions. Inspect the tables below for all values, limits, and source notes.

Density

7.2 g/cm³TYPICAL · temperature not stated

Thermal Conductivity

46 W/(m·K)TYPICAL · temperature not stated

Specific Heat Capacity

480 J/(kg·K)TYPICAL · temperature not stated

Composition Excerpt

C 3–3.3 wt%Carbon (range)

Standard Elemental Basis: RANGE

Engineering Summary

ASTM A48 Class 35 is a high-duty, fully pearlitic gray cast iron designed for demanding mechanical applications. Requiring a minimum tensile strength of 35 ksi (241 MPa) on separately cast Test Bar B, it features fine Type A graphite flakes and provides superior wear resistance, high compressive strength (~850 MPa), and excellent dimensional stability for heavy machine tool ways and compressor bodies.

ASTM A48 Class 35 Gray Cast Iron Documented Applications

›Heavy machine tool ways, saddles, and spindle housings
›Heavy truck brake drums and industrial clutch pressure plates
›Refrigeration and natural gas compressor cylinder liners
›Hydraulic pump bodies and pressure-containing castings

Recognized Aliases

Source-backed commercial trade name and short designations cataloged in canonical data.

Class 35 Gray IronSAE G3500 Gray Iron

ASTM A48 Class 35 Gray Cast Iron Specifications & Designations

Standard Designations & Applicable Specifications — Semantically classified designations distinguishing primary standard identifiers, commercial trade names, and applicable specification references.

Direct Standard DesignationsDIRECT DESIGNATION

3 Primary Identifiers

Scroll horizontally for full designation data

System	Identifier	Standard System Name	Classification Notes & Provenance
ASTMPRIMARY	A48 Class 35	ASTM International	—Ref: Standard Specifications for Gray and Ductile Cast Iron (ASTM A48/A48M, ASTM A536, EN 1561, EN 1563, ISO 185, ISO 1083, SAE J431, SAE J434, ASM Handbook Vol 1)
UNS	F12401	Unified Numbering System	—Ref: Standard Specifications for Gray and Ductile Cast Iron (ASTM A48/A48M, ASTM A536, EN 1561, EN 1563, ISO 185, ISO 1083, SAE J431, SAE J434, ASM Handbook Vol 1)
SAE	J431 G3500	SAE International	—Ref: Standard Specifications for Gray and Ductile Cast Iron (ASTM A48/A48M, ASTM A536, EN 1561, EN 1563, ISO 185, ISO 1083, SAE J431, SAE J434, ASM Handbook Vol 1)

Recognized Commercial Aliases & Trade NamesCOMMON ALIAS

2 Listed

Scroll horizontally for full alias classifications

Recognized Name / Alias	Classification	Technical Usage & Context
Class 35 Gray Iron	Commercial Alias	Colloquial or commercial industry synonym
SAE G3500 Gray Iron	Historical Alias	Colloquial or commercial industry synonym

Applicable Specifications & Product Form ReferencesSPECIFICATION REFERENCE

2 Applicable Standards

Scroll horizontally for full standard specifications

Standards Body	Specification Code	Specification Title / Scope	Relationship Type
ASTM	ASTM A48 / A48M	Standard Specification for Gray Iron Castings	Specification Reference
SAE	SAE J431	Automotive Gray Iron Castings (Grade G3500)	Specification Reference

Engineering Notice: Applicable specifications establish manufacturing requirements, dimensional tolerances, and test criteria for specific product forms (e.g. bus bar, wire, plate, pipe). They represent applicable technical standards, not alternative or equivalent alloy grades.

ASTM A48 Class 35 Gray Cast Iron Chemical Composition

Chemical Composition (Weight %) — Elemental limits and values from the cited source. Preserves exact semantic limits (minimums, maximums, and ranges).

Scroll horizontally for full elemental limits

Element	Symbol	Semantic Basis	Specified Value	Unit	Metallurgical Notes & Qualification	Data Status
Carbon	C	RANGE	3.00 – 3.30	wt%	Ref: ASTM International, CEN, ISO & ASM International Standards Technical Committees	VERIFIED
Silicon	Si	RANGE	1.80 – 2.20	wt%	Ref: ASTM International, CEN, ISO & ASM International Standards Technical Committees	VERIFIED
Manganese	Mn	RANGE	0.60 – 0.90	wt%	Ref: ASTM International, CEN, ISO & ASM International Standards Technical Committees	VERIFIED
Phosphorus	P	MAXIMUM	≤ 0.10	wt%	Ref: ASTM International, CEN, ISO & ASM International Standards Technical Committees	VERIFIED
Sulfur	S	MAXIMUM	≤ 0.12	wt%	Ref: ASTM International, CEN, ISO & ASM International Standards Technical Committees	VERIFIED
Iron	Fe	REMAINDER	Remainder	wt%	Ref: ASTM International, CEN, ISO & ASM International Standards Technical Committees	VERIFIED

* Elemental percentages are expressed in weight percent (wt%). Values represent applicable specification limits. Unspecified trace elements are not fabricated or assumed.Preserves exact semantic basis

Property Display UnitsSwitch between Canonical SI and Source / US Customary units:

ASTM A48 Class 35 Gray Cast Iron Physical Properties

Source-specific physical properties. Test temperatures are shown only where reported.

1 Parameters

Scroll horizontally for full property parameters

Property Parameter	Canonical SI Value	Semantic Basis	Test Temperature / Context Range	Source Raw Reference	Source Reference	Status
Density	7.2 g/cm³	TYPICAL		7.2 g/cm³	ASTM International, CEN & ISO Technical Committees	VERIFIED

ASTM A48 Class 35 Gray Cast Iron Thermal & Thermodynamic Properties

Phase change temperatures, thermal conductivity, specific heat, mean coefficients of thermal expansion across standardized temperature ranges, and recommended thermal processing windows.

3 Parameters

Scroll horizontally for full property parameters

Property Parameter	Canonical SI Value	Semantic Basis	Source Raw Reference	Source Reference	Status
Thermal Conductivity	46 W/(m·K)	TYPICAL	46 W/(m·K)	ASTM International, CEN & ISO Technical Committees	VERIFIED
Specific Heat Capacity	480 J/(kg·K)	TYPICAL	480 J/(kg·K)	ASTM International, CEN & ISO Technical Committees	VERIFIED
Coefficient of Thermal Expansion	11 µm/(m·K)	TYPICAL	11 µm/(m·K)	ASTM International, CEN & ISO Technical Committees	VERIFIED

ASTM A48 Class 35 Gray Cast Iron Electrical Properties

Electrical conductivity and resistivity in their reported units and conditions.

1 Parameters

Scroll horizontally for full property parameters

Property Parameter	Canonical SI Value	Semantic Basis	Test Temperature / Context Range	Source Raw Reference	Source Reference	Status
Electrical Resistivity	650 nΩ·m	TYPICAL		650 nΩ·m	ASTM International, CEN & ISO Technical Committees	VERIFIED

ASTM A48 Class 35 Gray Cast Iron Mechanical Properties

Contextual Mechanical Properties & Tempers: Engineering strength, ductility, and hardness values grouped by product form, temper, and section thickness. Mechanical properties are contextual and not isotropic averages.

Elastic & Baseline Mechanical ConstantsSource-specific measurement conditions

Poisson Ratio

0.26 dimensionless

Showing 3 of 3 conditions

Scroll horizontally for all conditions & tempers

Product Form	Temper / Condition	Section Size	Tensile (UTS)	Yield Strength	Elongation	Shear Strength	Fatigue Strength	Hardness (Scales Preserved)	Status
Standard Product Form	As-Cast Source values and qualifiers Ultimate Tensile Strength: ≥ 241 MPa (MINIMUM)Governing minimum tensile strength per ASTM A48 Class 35 (35 ksi = 241 MPa). No distinct yield point.ASTM International, CEN, ISO & ASM International Standards Technical Committees — ASTM A48, ASTM A536, EN 1561, EN 1563, ISO 185, ISO 1083, SAE J431, SAE J434, ASM Handbook Vol 1	30.5 mm Test Bar B	≥ 241 MPa	—	—	—	—	—	VERIFIED
Standard Product Form	As-Cast Source values and qualifiers Modulus of Elasticity: 105 GPa (TYPICAL)ASTM International, CEN, ISO & ASM International Standards Technical Committees — ASTM A48, ASTM A536, EN 1561, EN 1563, ISO 185, ISO 1083, SAE J431, SAE J434, ASM Handbook Vol 1	—	—	—	—	—	—	—	VERIFIED
Standard Product Form	As-Cast Source values and qualifiers HBW Hardness: 195–245 HBW (RANGE)10/3000ASTM International, CEN, ISO & ASM International Standards Technical Committees — ASTM A48, ASTM A536, EN 1561, EN 1563, ISO 185, ISO 1083, SAE J431, SAE J434, ASM Handbook Vol 1	—	—	—	—	—	—	195–245 HBW	VERIFIED

Hardness Integrity Notice: Rockwell B (HRB), Rockwell F (HRF), and Superficial 30T (HR30T) scales are reported on their measured scales without cross-scale mathematical conversion.

Source: See fact-level citations

ASTM A48 Class 35 Gray Cast Iron Processing & Fabrication

Machining, joining, forming, and thermal processing ratings cataloged from the cited authoritative technical reference.

Source: ASTM International, CEN, ISO & ASM International Standards Technical Committees

Machinability

Very good machinability (~80% relative to C36000 baseline). Fully pearlitic matrix causes slightly higher tool wear than Class 30.

Weldability & Joining

Poor weldability. High risk of cracking; requires strict 300°C preheat and nickel-based filler metals.

Heat Treatment & Working Ranges

Stress relief annealing at 565°C–595°C for 2 hours. Flame and induction surface hardening can achieve 52–56 HRC on slideway surfaces.

Forming & Cold Working

Non-deformable. Cast iron cannot be cold or hot formed.

ASTM A48 Class 35 Gray Cast Iron Equivalent & Comparable Grades

Comparable Grades & Cross-References: Carefully classified cross-reference relationships for ASTM A48 Class 35 Gray Cast Iron. Comparable does not mean equivalent.

Scroll horizontally for relationship classifications & comparisons

Related Material	Family	Relationship Classification	Metallurgical Notes & Differences	Status	Action
ASTM A48 Class 40 Gray Cast Iron	Cast Iron	Commonly Compared	Class 35 provides slightly easier foundry gating and lower chilling in sections below 15 mm, while Class 40 is chosen when tensile loads reach 276 MPa.Materials serve different design priorities (e.g. higher strength vs superior corrosion resistance or cost).	VERIFIED	Side-by-Side Compare →

Related Engineering & Metallurgy Guides

Contextual technical guides explaining degradation mechanisms, testing methodologies, and selection criteria relevant to ASTM A48 Class 35 Gray Cast Iron.

Corrosion & Surface Engineering15 min read

How to Remove Rust From Cast Iron: Methods, Science & Prevention

Cast iron is an indispensable alloy family renowned for superior vibration damping and castability, but its iron matrix and carbon microstructure make it susceptible to atmospheric rust. Restoring rusted cast iron requires understanding how mechanical and chemical methods interact with the underlying metal.

Author: MatGrades Materials Engineering GroupRead Guide →

Sources

Sources & Provenance Trail: Authoritative reference publications, standards specifications, and data registers cited across this material record.

ASTM International, CEN & ISO Technical CommitteesStandard Specifications for Gray and Ductile Cast Iron (ASTM A48/A48M, ASTM A536, EN 1561, EN 1563, ISO 185, ISO 1083, SAE J431, SAE J434, ASM Handbook Vol 1)

STANDARDS ORG

Authoritative foundry data harmonized across ASTM A48, ASTM A536, EN 1561, EN 1563, ISO 185, ISO 1083, SAE J431, SAE J434, and ASM International Handbook Volume 1 (Properties and Selection: Irons, Steels, and High-Performance Alloys).

Issuing Body: ASTM International, CEN, ISO & ASM International Standards Technical CommitteesRevision: ASTM A48/A48M-22 / ASTM A536-84(2024) / EN 1561:2020 / EN 1563:2018 / ISO 185:2020 / ISO 1083:2018View Source Record ↗