Aluminum & Aluminum Alloys•Wrought Aluminum Alloys•

VERIFIED(Source-Verified)

1100 Aluminum

Primary Designation:AA 1100

Aliases:

AA 1100Al 1100

Mat Grades internal verification confirms source-backed fidelity and data integrity. It does not constitute external certification or guaranteed lot conformity. Read engineering disclaimer →

Download PDF Download Excel

Data Completeness:7 composition elements and 25 condition-specific property values cataloged.

Omitted fields represent unverified properties. "Missing is better than invented."

Key Engineering Properties

Representative source rows, qualified by their reported conditions. Inspect the tables below for all values, limits, and source notes.

Density

2.71 g/cm³TYPICAL · temperature not stated

Electrical Conductivity

59 % IACSTYPICAL · O Temper · temperature not stated

Thermal Conductivity

222 W/(m·K)TYPICAL · O Temper · temperature not stated

Melting Range (Solidus / Liquidus)

643 – 657 °C643 – 657 °F

Solidus: 643°C | Liquidus: 657°C

Composition Excerpt

Cu 0.05–0.2 wt%Copper (range)

Standard Elemental Basis: RANGE

Tensile Strength

90 MPaTYPICAL · O Temper · temperature not stated

Reported: 90

Engineering Summary

1100 is commercially pure wrought aluminum (minimum 99.00% Al) with excellent corrosion resistance, high thermal and electrical conductivity, and superior formability and weldability. Mechanical properties are determined by cold work rather than precipitation hardening.

Recognized Aliases

Source-backed commercial trade name and short designations cataloged in canonical data.

AA 1100Al 1100

1100 Aluminum Specifications & Designations

Standard Designations & Applicable Specifications — Semantically classified designations distinguishing primary standard identifiers, commercial trade names, and applicable specification references.

Direct Standard DesignationsDIRECT DESIGNATION

3 Primary Identifiers

Scroll horizontally for full designation data

System	Identifier	Standard System Name	Classification Notes & Provenance
AAPRIMARY	1100	Aluminum Association	—Ref: Kaiser Aluminum Technical Engineering Datasheet
UNS	A91100	Unified Numbering System	—Ref: Kaiser Aluminum Technical Engineering Datasheet
ISO	Al99.0Cu	International Organization for Standardization	—Ref: Kaiser Aluminum Technical Engineering Datasheet

Recognized Commercial Aliases & Trade NamesCOMMON ALIAS

2 Listed

Scroll horizontally for full alias classifications

Recognized Name / Alias	Classification	Technical Usage & Context
AA 1100	Commercial Alias	Colloquial or commercial industry synonym
Al 1100	Commercial Alias	Colloquial or commercial industry synonym

Applicable Specifications & Product Form ReferencesSPECIFICATION REFERENCE

2 Applicable Standards

Scroll horizontally for full standard specifications

Standards Body	Specification Code	Specification Title / Scope	Relationship Type
ASTM International	ASTM B210	Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless TubesPRODUCT_SPECIFICATION · Product form: Drawn Tube	Specification Reference
ASTM International	ASTM B221	Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and TubesPRODUCT_SPECIFICATION · Product form: Extrusions	Specification Reference

Engineering Notice: Applicable specifications establish manufacturing requirements, dimensional tolerances, and test criteria for specific product forms (e.g. bus bar, wire, plate, pipe). They represent applicable technical standards, not alternative or equivalent alloy grades.

1100 Aluminum Chemical Composition

Chemical Composition (Weight %) — Elemental limits and values from the cited source. Preserves exact semantic limits (minimums, maximums, and ranges).

Scroll horizontally for full elemental limits

Element	Symbol	Semantic Basis	Specified Value	Unit	Metallurgical Notes & Qualification	Data Status
Copper	Cu	RANGE	0.05 – 0.20	wt%	Ref: Kaiser Aluminum Corporation	VERIFIED
Manganese	Mn	MAXIMUM	≤ 0.05	wt%	Ref: Kaiser Aluminum Corporation	VERIFIED
Zinc	Zn	MAXIMUM	≤ 0.10	wt%	Ref: Kaiser Aluminum Corporation	VERIFIED
Silicon plus Iron	Si + Fe	MAXIMUM	≤ 0.95	wt%	Combined Si+Fe limit per AA standardRef: Kaiser Aluminum Corporation	VERIFIED
Other Elements Each	OE	EACH	≤ 0.05 each	wt%	Ref: Kaiser Aluminum Corporation	VERIFIED
Other Elements Total	OT	TOTAL	≤ 0.15	wt%	Ref: Kaiser Aluminum Corporation	VERIFIED
Aluminum	Al	REMAINDER	Remainder	wt%	Balance aluminum (99.00% minimum)Ref: Kaiser Aluminum Corporation	VERIFIED

* Elemental percentages are expressed in weight percent (wt%). Values represent applicable specification limits. Unspecified trace elements are not fabricated or assumed.Preserves exact semantic basis

Property Display UnitsSwitch between Canonical SI and Source / US Customary units:

1100 Aluminum Physical Properties

Source-specific physical properties. Test temperatures are shown only where reported.

1 Parameters

Scroll horizontally for full property parameters

Property Parameter	Canonical SI Value	Semantic Basis	Test Temperature / Context Range	Source Raw Reference	Source Reference	Status
Density	2.71 g/cm³	TYPICAL		2.71 g/cm³	Kaiser Aluminum Corporation	VERIFIED

1100 Aluminum Thermal & Thermodynamic Properties

Phase change temperatures, thermal conductivity, specific heat, mean coefficients of thermal expansion across standardized temperature ranges, and recommended thermal processing windows.

4 Parameters

Scroll horizontally for full property parameters

Property Parameter	Canonical SI Value	Semantic Basis	Source Raw Reference	Source Reference	Status
Coefficient of Thermal Expansion	23.6 µm/(m·K)	TYPICAL	23.6 µm/(m·K)	Kaiser Aluminum Corporation	VERIFIED
Solidus Temperature	643 °C	TYPICAL	643 °C	Kaiser Aluminum Corporation	VERIFIED
Liquidus Temperature	657 °C	TYPICAL	657 °C	Kaiser Aluminum Corporation	VERIFIED
Thermal ConductivityCondition: O Temper	222 W/(m·K)	TYPICAL	222 W/(m·K)	Kaiser Aluminum Corporation	VERIFIED

1100 Aluminum Electrical Properties

Electrical conductivity and resistivity in their reported units and conditions.

1 Parameters

Scroll horizontally for full property parameters

Property Parameter	Canonical SI Value	Semantic Basis	Test Temperature / Context Range	Source Raw Reference	Source Reference	Status
Electrical ConductivityCondition: O Temper	59 % IACS	TYPICAL		59.0 % IACS	Kaiser Aluminum Corporation	VERIFIED

1100 Aluminum Mechanical Properties

Contextual Mechanical Properties & Tempers: Engineering strength, ductility, and hardness values grouped by product form, temper, and section thickness. Mechanical properties are contextual and not isotropic averages.

Elastic & Baseline Mechanical ConstantsSource-specific measurement conditions

Modulus of Elasticity

69 GPa

Temper / Condition:

Showing 3 of 3 conditions

Scroll horizontally for all conditions & tempers

Product Form	Temper / Condition	Section Size	Tensile (UTS)	Yield Strength	Elongation	Shear Strength	Fatigue Strength	Hardness (Scales Preserved)	Status
Drawn Tube	O Temper Source values and qualifiers Ultimate Tensile Strength: 90 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties O Drawn Tube Yield Strength (0.2% Offset): 34 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties O Drawn Tube Elongation (4D): 35 % (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties O Drawn Tube Shear Strength: 62 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties O Drawn Tube Fatigue Endurance Limit (5x10^8 cycles): 34 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties O Drawn Tube HB Hardness: 23 HB (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Hardness O Drawn Tube O	—	90 MPa	34 MPa	35 %	62 MPa	34 MPa	23 HB	VERIFIED
Drawn Tube	H14 Temper Source values and qualifiers Ultimate Tensile Strength: 124 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties H14 Drawn Tube Yield Strength (0.2% Offset): 117 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties H14 Drawn Tube Elongation (4D): 20 % (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties H14 Drawn Tube Shear Strength: 76 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties H14 Drawn Tube Fatigue Endurance Limit (5x10^8 cycles): 48 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties H14 Drawn Tube HB Hardness: 32 HB (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Hardness H14 Drawn Tube H14	—	124 MPa	117 MPa	20 %	76 MPa	48 MPa	32 HB	VERIFIED
Drawn Tube	H18 Temper Source values and qualifiers Ultimate Tensile Strength: 165 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties H18 Drawn Tube Yield Strength (0.2% Offset): 152 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties H18 Drawn Tube Elongation (4D): 15 % (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties H18 Drawn Tube Shear Strength: 90 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties H18 Drawn Tube Fatigue Endurance Limit (5x10^8 cycles): 62 MPa (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Mechanical Properties H18 Drawn Tube HB Hardness: 44 HB (TYPICAL)Kaiser Aluminum Corporation — mat-phase4c-1100 Hardness H18 Drawn Tube H18	—	165 MPa	152 MPa	15 %	90 MPa	62 MPa	44 HB	VERIFIED

Hardness Integrity Notice: Rockwell B (HRB), Rockwell F (HRF), and Superficial 30T (HR30T) scales are reported on their measured scales without cross-scale mathematical conversion.

Source: See fact-level citations

Practical Engineering & Fabrication Notes

By Mat Grades Editorial Desk · Updated 2026-11-14. Use alongside the specified product standard and supplier certificate.

Machining & shop-floor behavior

For 1100 Aluminum, a qualified cutting-speed or tool-life recommendation is not supplied in the available record. A relevant hardness example is HB Hardness: 23 HB (typical; O Temper, O, Drawn Tube). Use that supplied condition for a trial of the difficult feature. Record tool changes, burr removal, unclamped dimensions and accepted parts per hour. Relative machinability ratings from different reference scales should not be compared as if they were one common test.

Weldability, brazing & joining

No qualified weld procedure, filler selection or preheat/interpass schedule is established by this material record. Obtain a procedure for the actual joint, supplied condition and section rather than copying one from a nearby grade. The first cataloged strength example is Ultimate Tensile Strength: 90 MPa (typical; O Temper, O, Drawn Tube). Assess the final part after joining or thermal processing. Include distortion, cleanup and inspection in the quotation. A material designation or favorable process rating is a starting point for qualification, not evidence that an untested joint meets the drawing.

Corrosion & service environment

Review the finish, moisture traps and contact with other metals before accepting an assembly for service. Alloy, temper and surface treatment answer different questions. A stronger listed condition does not automatically solve corrosion, wear or deflection, and thermal-property data is not a maximum operating-temperature rating. The recorded thermal example is Coefficient of Thermal Expansion: 23.6 µm/(m·K) (typical; additional condition not stated). State the exposure and inspection access in the design record so that a change of installation or cleaning method triggers a review. The selected composition entries are Cu 0.05–0.2 wt%, Mn maximum 0.05 wt%, Zn maximum 0.1 wt%. Chemistry documents identity; it does not establish fluid compatibility.

Selection trade-offs & applications

Use AA 1100, UNS A91100, ISO Al99.0Cu to identify the candidate, then specify the product form and delivered condition separately. A specific component application is not asserted where the source record does not provide one. The listed forms include Drawn Tube; confirm the actual stock offered by the supplier. Compare the complete route through machining, joining, finish and inspection. Keep the certificate, required test location and acceptance criteria with the first-article record. A later change of grade, condition or source should be assessed against that same requirement.

Technical references: Kaiser Aluminum Corporation

1xxx Series Wrought Aluminum Alloys

Wrought aluminum alloys grouped under the 1xxx metallurgical series sharing fundamental alloying systems and physical characteristics.

2 Adjacent Grades

1050

1050 Aluminum

View Grade →

1100Current Grade

1100 Aluminum

Related Engineering & Metallurgy Guides

Contextual technical guides explaining degradation mechanisms, testing methodologies, and selection criteria relevant to 1100 Aluminum.

Welding & Fabrication18 min read

How to Weld Aluminium to Aluminium: TIG, MIG, Filler Metals & Alloy Guide

Aluminium possesses distinct physical and metallurgical properties—including a tenacious refractory oxide layer that melts at 2,072°C, thermal conductivity five times higher than structural steel, extreme liquid hydrogen solubility, and a lack of visible color change before melting. Successful aluminium-to-aluminium welding requires matching the base alloy series to an appropriate process (AC TIG, pulsed MIG, or SMAW) and compatible filler metal while designing for unavoidable heat-affected zone softening.

Author: Mat Grades Editorial DeskRead Guide →

Sources

Sources & Provenance Trail: Authoritative reference publications, standards specifications, and data registers cited across this material record.

Kaiser Aluminum CorporationKaiser Aluminum Technical Engineering Datasheet

PRIMARY PRODUCER

Reviewed factual transcription from Kaiser Aluminum technical product datasheets: mat-phase4c-1100 Chemical Composition Limits. Selected facts only; no decorative text or full standard tables reproduced.