SAE 1022 Carbon Steel
Mat Grades internal verification confirms source-backed fidelity and data integrity. It does not constitute external certification or guaranteed lot conformity. Read engineering disclaimer →
Key Engineering Properties
Representative source rows, qualified by their reported conditions. Inspect the tables below for all values, limits, and source notes.
Engineering Summary
SAE 1022 is a low-carbon carburizing grade with manganese up to 1.00%, widely used for self-tapping screws, fasteners, and cold-extruded components requiring high surface hardness.
Recognized Aliases
Source-backed commercial trade name and short designations cataloged in canonical data.
SAE 1022 Carbon Steel Specifications & Designations
Standard Designations & Applicable Specifications — Semantically classified designations distinguishing primary standard identifiers, commercial trade names, and applicable specification references.
| System | Identifier | Standard System Name | Classification Notes & Provenance |
|---|---|---|---|
| SAEPRIMARY | 1022 | Society of Automotive Engineers | —Ref: Practical Data for Metallurgists, 19th edition |
| AISI | 1022 | American Iron and Steel Institute | —Ref: Practical Data for Metallurgists, 19th edition |
| UNS | G10220 | Unified Numbering System | —Ref: Practical Data for Metallurgists, 19th edition |
| Standards Body | Specification Code | Specification Title / Scope | Relationship Type |
|---|---|---|---|
| SAE | SAE 1022 Carbon Steel Engineering Datasheet | Applicable specification reference. | Specification Reference |
SAE 1022 Carbon Steel Chemical Composition
Chemical Composition (Weight %) — Elemental limits and values from the cited source. Preserves exact semantic limits (minimums, maximums, and ranges).
| Element | Symbol | Atomic No. | Semantic Basis | Specified Value | Unit | Metallurgical Notes & Qualification | Data Status |
|---|---|---|---|---|---|---|---|
| Iron | Fe | 26 | BALANCE | Balance | wt% | Ref: Metallus | VERIFIED |
| Carbon | C | 6 | RANGE | 0.18 – 0.23 | wt% | Ref: Metallus | VERIFIED |
| Manganese | Mn | 25 | RANGE | 0.70 – 1.00 | wt% | Ref: Metallus | VERIFIED |
| Phosphorus | P | 15 | MAXIMUM | ≤ 0.03 | wt% | Ref: Metallus | VERIFIED |
| Sulfur | S | 16 | MAXIMUM | ≤ 0.04 | wt% | Ref: Metallus | VERIFIED |
SAE 1022 Carbon Steel Physical Properties
Source-specific physical properties. Test temperatures are shown only where reported.
| Property Parameter | Canonical SI Value | Semantic Basis | Test Temperature / Context Range | Source Raw Reference | Source Reference | Status |
|---|---|---|---|---|---|---|
| Density | 7.87 g/cm³ | TYPICAL | 7.87 g/cm³ | Metallus | VERIFIED | |
| Elastic Modulus | 205 GPa | TYPICAL | 205 GPa | Metallus | VERIFIED | |
| Poisson's Ratio | 0.29 dimensionless | TYPICAL | 0.29 dimensionless | Metallus | VERIFIED |
SAE 1022 Carbon Steel Thermal & Thermodynamic Properties
Phase change temperatures, thermal conductivity, specific heat, mean coefficients of thermal expansion across standardized temperature ranges, and recommended thermal processing windows.
| Property Parameter | Canonical SI Value | Semantic Basis | Test Temperature / Context Range | Source Raw Reference | Source Reference | Status |
|---|---|---|---|---|---|---|
| Specific Heat Capacity | 486 J/(kg·K) | TYPICAL | 486 J/(kg·K) | Metallus | VERIFIED | |
| Thermal Conductivity | 51.9 W/(m·K) | TYPICAL | 51.9 W/(m·K) | Metallus | VERIFIED |
SAE 1022 Carbon Steel Mechanical Properties
Contextual Mechanical Properties & Tempers: Engineering strength, ductility, and hardness values grouped by product form, temper, and section thickness. Mechanical properties are contextual and not isotropic averages.
| Product Form | Temper / Condition | Section Size | Tensile (UTS) | Yield Strength | Elongation | Shear Strength | Fatigue Strength | Hardness (Scales Preserved) | Status |
|---|---|---|---|---|---|---|---|---|---|
| Bar | Cold Drawn Bar (19 to 32 mm)Source values and qualifiersUltimate Tensile Strength: ≥ 490 MPa (MINIMUM)ASTM A108 / ASTM E8Metallus — p118, Estimated Minimum Properties for Cold Drawn Bars Reduction of Area: ≥ 40 % (MINIMUM)ASTM A108 / ASTM E8Metallus — p118, Estimated Minimum Properties for Cold Drawn Bars | — | ≥ 490 MPa | — | — | — | — | — | VERIFIED |
| Bar | Cold Drawn Bar (19 to 32 mm)Source values and qualifiersYield Strength: ≥ 405 MPa (MINIMUM)ASTM A108 / ASTM E8 (0.2% offset)Metallus — p118, Estimated Minimum Properties for Cold Drawn Bars | — | — | ≥ 405 MPa | — | — | — | — | VERIFIED |
| Bar | Cold Drawn Bar (19 to 32 mm)Source values and qualifiersElongation at Break: ≥ 15 % (MINIMUM)ASTM A108 / ASTM E8Metallus — p118, Estimated Minimum Properties for Cold Drawn Bars | — · in 50 mm (2 in) | — | — | ≥ 15 % | — | — | — | VERIFIED |
| Bar | Cold Drawn Bar (19 to 32 mm)Source values and qualifiersHB Hardness: ≤ 167 HB (TYPICAL)Metallus — p118, Estimated Minimum Properties for Cold Drawn Bars | — | — | — | — | — | — | ≤ 167 HB | VERIFIED |
SAE 1022 Carbon Steel Equivalent & Comparable Grades
Comparable Grades & Cross-References: Carefully classified cross-reference relationships for SAE 1022 Carbon Steel. Comparable does not mean equivalent.
| Related Material | Family | Relationship Classification | Metallurgical Notes & Differences | Status | Action |
|---|---|---|---|---|---|
| SAE 1020 Carbon Steel | Steel | Commonly Compared | Carburizing carbon steel with elevated manganese (0.70-1.00% Mn), standard for high-strength case-hardened tapping screws and cold-formed bolts.Materials serve different design priorities (e.g. higher strength vs superior corrosion resistance or cost). | VERIFIED | Side-by-Side Compare → |
SAE/AISI Low-Carbon Steel Cluster (1006–1026)
Plain carbon engineering steels with <0.26% C. Ordered by increasing nominal carbon content, illustrating the transition from maximum cold-formability to structural strength.
Sources
Sources & Provenance Trail: Authoritative reference publications, standards specifications, and data registers cited across this material record.
Reviewed factual transcription from primary producer engineering technical literature.
Reviewed factual transcription from primary producer engineering technical literature.
Reviewed factual transcription from primary producer engineering technical literature.
Reviewed factual transcription from primary producer engineering technical literature.