1. Identity, Classification & Standards

Parameter	C26000 Cartridge Brass 70/30	C28000 Muntz Metal 60/40
Material Family	Copper Alloys	Copper Alloys
Subfamily	Cartridge Brass	Yellow Brass
UNS Designation	C26000	C28000
COMMERCIAL Designation	Cartridge Brass	Muntz Metal 60/40
CDA Designation	Alloy 260	Alloy 280
SPECIFICATION Designation	ASTM B36/B36M	ASTM B36/B36M

2. Chemical Composition Limits (wt %)Source-specific limits and typical values

Element	C26000 Cartridge Brass 70/30	C28000 Muntz Metal 60/40
Cu (Copper)	68.5 – 71.5%	59 – 63%
Pb (Lead)	≤ 0.07%	≤ 0.09%
Zn (Zinc)	Bal.	Bal.
Fe (Iron)	≤ 0.05%	≤ 0.07%

3. Physical Properties

Property	C26000 Cartridge Brass 70/30	C28000 Muntz Metal 60/40
Density · TYPICAL · 20 °CUnit: g/cm³	8.525 g/cm³	8.387 g/cm³

4. Contextual Mechanical PropertiesUnit: SI

Mechanical Parameter	C26000 Cartridge Brass 70/301/2 Hard (H02)	C28000 Muntz Metal 60/401/2 Hard (H02)
Modulus of Elasticity (Tension) · TYPICALUnit: GPa	110.3 GPa	103.4 GPa
Modulus of Rigidity · TYPICALUnit: MPa	41368.5 MPa	38610.6 MPa
Machinability Rating · TYPICALUnit: %	30 %	40 %
Tensile Strength · Flat Products · 0.04 · 1/2 Hard (H02) · TYPICAL · 20 °CUnit: MPa	427.5 MPa	482.6 MPa
Tensile Strength · Rod · 1 · 1/2 Hard (H02) · TYPICAL · 20 °CUnit: MPa	482.6 MPa	— MPa
Elongation · Flat Products · 0.04 · 1/2 Hard (H02) · TYPICAL · 20 °CUnit: %	25 %	10 %
Elongation · Rod · 1 · 1/2 Hard (H02) · TYPICAL · 20 °CUnit: %	30 %	— %
Shear Strength · Flat Products · 0.04 · 1/2 Hard (H02) · TYPICALUnit: MPa	275.8 MPa	303.4 MPa
Shear Strength · Rod · 1 · 1/2 Hard (H02) · TYPICALUnit: MPa	289.6 MPa	— MPa
Fatigue Strength · Flat Products · 0.04 · 1/2 Hard (H02) · TYPICALUnit: MPa	124.1 MPa	— MPa
Fatigue Strength · Rod · 1 · 1/2 Hard (H02) · TYPICALUnit: MPa	151.7 MPa	— MPa
Yield Strength (0.5% Ext) · Flat Products · 0.04 · 1/2 Hard (H02) · TYPICAL · 20 °CUnit: MPa	— MPa	344.7 MPa
Forgeability Rating · TYPICALUnit: —	— —	90 —

5. Electrical & Thermal Conductive Properties

Property	C26000 Cartridge Brass 70/30	C28000 Muntz Metal 60/40
Electrical Conductivity · TYPICAL · 20 °CCategory: ELECTRICAL • Unit: % IACS	28 % IACS	28 % IACS
Liquidus Temperature · TYPICALCategory: THERMAL • Unit: °C	954.4 °C	904.4 °C
Solidus Temperature · TYPICALCategory: THERMAL • Unit: °C	915.6 °C	898.9 °C
Thermal Conductivity · TYPICAL · 20 °CCategory: THERMAL • Unit: W/(m·K)	121.15 W/(m·K)	122.88 W/(m·K)
Coefficient of Thermal Expansion (CTE) · TYPICALCategory: THERMAL • Unit: µm/(m·K)	19.98 µm/(m·K)	20.88 µm/(m·K)
Specific Heat Capacity · TYPICAL · 20 °CCategory: THERMAL • Unit: J/(kg·K)	376.8 J/(kg·K)	376.8 J/(kg·K)
Annealing Temperature Range · RANGECategory: THERMAL • Unit: °C	426.7–760 °C	426.7–593.3 °C
Hot Working Temperature Range · RANGECategory: THERMAL • Unit: °C	732.2–843.3 °C	621.1–787.8 °C

6. Hardness Evaluation (Discrete Scales Preserved)No cross-scale mathematical conversion

Hardness Scale	C26000 Cartridge Brass 70/30	C28000 Muntz Metal 60/40
Rockwell B Hardness · Flat Products · 0.04 · 1/2 Hard (H02) · TYPICAL	70 HRB	75 HRB
Rockwell B Hardness · Rod · 1 · 1/2 Hard (H02) · TYPICAL	80 HRB	—
Rockwell 30T Hardness · Flat Products · 0.04 · 1/2 Hard (H02) · TYPICAL	65 HR30T	67 HR30T

7. Fabrication & Processing Comparison

C26000 Cartridge Brass 70/30 Characteristics:

Machinability: Machinability rating: 30% relative to free-cutting brass (C36000 = 100%).

Weldability: Soldering: Excellent; Brazing: Excellent; Oxyacetylene Welding: Good; Gas Shielded Arc Welding: Good; Coated Metal Arc Welding: Not Recommended; Spot Weld: Fair; Seam Weld: Not Recommended; Butt Weld: Good

Formability / Cold Working: Capacity for Being Cold Worked: Excellent. Capacity for Being Hot Formed: Fair.

Heat Treatment & Annealing: Annealing temperature range: 426.7°C to 760.0°C (800°F - 1400°F). Hot working temperature range: 732.2°C to 843.3°C (1350°F - 1550°F).

C28000 Muntz Metal 60/40 Characteristics:

Machinability: Machinability rating: 40% relative to free-cutting brass (C36000 = 100%). Forgeability rating: 90.

Weldability: Soldering: Excellent; Brazing: Excellent; Oxyacetylene Welding: Good; Gas Shielded Arc Welding: Fair; Coated Metal Arc Welding: Not Recommended; Spot Weld: Good; Seam Weld: Not Recommended; Butt Weld: Good

Formability / Cold Working: Capacity for Being Cold Worked: Fair. Capacity for Being Hot Formed: Excellent.

Heat Treatment & Annealing: Annealing temperature range: 426.7°C to 593.3°C (800°F - 1100°F). Hot working temperature range: 621.1°C to 787.8°C (1150°F - 1450°F).

← View Complete C26000 Cartridge Brass 70/30 Specification View Complete C28000 Muntz Metal 60/40 Specification →