Material Comparison
Compare verified engineering materials side by side with condition-specific mechanical properties.
| Parameter | EN-GJL-200 Gray Cast Iron | ASTM A48 Class 30 Gray Cast Iron |
|---|---|---|
| Material Family | Cast Iron | Cast Iron |
| Subfamily | Gray Cast Iron | Gray Cast Iron |
| EN Designation | EN-GJL-200 | — |
| W-Nr Designation | EN-JL1030 | — |
| DIN Designation | GG-20 | — |
| ISO Designation | 185/JL/200 | — |
| ASTM Designation | — | A48 Class 30 |
| UNS Designation | — | F12101 |
| SAE Designation | — | J431 G3000 |
| Element | EN-GJL-200 Gray Cast Iron | ASTM A48 Class 30 Gray Cast Iron |
|---|---|---|
| C (Carbon) | 3.2 – 3.5% | 3.1 – 3.4% |
| Si (Silicon) | 2 – 2.5% | 1.9 – 2.3% |
| Mn (Manganese) | 0.6 – 0.9% | 0.6 – 0.9% |
| P (Phosphorus) | ≤ 0.15% | ≤ 0.12% |
| S (Sulfur) | ≤ 0.15% | ≤ 0.15% |
| Fe (Iron) | — | — |
| Property | EN-GJL-200 Gray Cast Iron | ASTM A48 Class 30 Gray Cast Iron |
|---|---|---|
| Density · TYPICALUnit: g/cm³ | 7.15 g/cm³ | 7.2 g/cm³ |
| Mechanical Parameter | EN-GJL-200 Gray Cast IronAs-Cast (Wall thickness 15 mm to 30 mm) | ASTM A48 Class 30 Gray Cast IronAs-Cast (Standard Test Bar B, 30.5 mm diameter) |
|---|---|---|
| Poisson Ratio · TYPICALUnit: dimensionless | 0.26 dimensionless | 0.26 dimensionless |
| Property | EN-GJL-200 Gray Cast Iron | ASTM A48 Class 30 Gray Cast Iron |
|---|---|---|
| Electrical Resistivity · TYPICALCategory: ELECTRICAL • Unit: nΩ·m | 700 nΩ·m | 680 nΩ·m |
| Thermal Conductivity · TYPICALCategory: THERMAL • Unit: W/(m·K) | 49 W/(m·K) | — W/(m·K) |
| Thermal Conductivity · TYPICAL · 20 °CCategory: THERMAL • Unit: W/(m·K) | — W/(m·K) | 48 W/(m·K) |
| Specific Heat Capacity · TYPICALCategory: THERMAL • Unit: J/(kg·K) | 470 J/(kg·K) | 480 J/(kg·K) |
| Coefficient of Thermal Expansion · TYPICALCategory: THERMAL • Unit: µm/(m·K) | 11.2 µm/(m·K) | 11 µm/(m·K) |
Machinability: Very good machinability (~95% relative to C36000 baseline). Natural graphite flake lubrication.
Weldability: Poor weldability. Repair welding requires preheat of 250°C–300°C and nickel-based electrodes.
Formability / Cold Working: Non-deformable.
Heat Treatment & Annealing: Stress relief at 540°C–580°C.
Machinability: Excellent machinability (~90% relative to C36000 free-cutting brass). Flake graphite acts as internal lubricant and natural chip breaker. Readily turned, milled, and drilled without burr formation.
Weldability: Poor weldability. Arc welding produces brittle martensitic heat-affected zones and crack risks. Recommended repair procedure requires 250°C–350°C (480°F–660°F) preheat, nickel-iron (ENiFe-CI) electrodes, short beads with peening, and slow insulation cooling.
Formability / Cold Working: Non-deformable. Gray cast iron is inherently brittle in tension and cannot be cold or hot deformed.
Heat Treatment & Annealing: Stress relief annealing at 540°C–595°C (1000°F–1100°F) for 1–2 hours eliminates residual casting stresses and prevents distortion. Flame or induction surface hardening can achieve 50–55 HRC on slideways.