1. Identity, Classification & Standards
| Parameter | SAE 1015 Carbon Steel | SAE 1006 Carbon Steel |
|---|---|---|
| Material Family | Steel | Steel |
| Subfamily | Carbon Steel | Carbon Steel |
| SAE Designation | 1015 | 1006 |
| AISI Designation | 1015 | 1006 |
| UNS Designation | G10150 | G10060 |
| SPECIFICATION Designation | SAE 1015 Carbon Steel Engineering Datasheet | SAE 1006 Carbon Steel Engineering Datasheet |
2. Chemical Composition Limits (wt %)Source-specific limits and typical values
| Element | SAE 1015 Carbon Steel | SAE 1006 Carbon Steel |
|---|---|---|
| Fe (Iron) | Bal. | Bal. |
| C (Carbon) | 0.13 – 0.18% | ≤ 0.08% |
| Mn (Manganese) | 0.3 – 0.6% | 0.25 – 0.4% |
| P (Phosphorus) | ≤ 0.03% | ≤ 0.03% |
| S (Sulfur) | ≤ 0.035% | ≤ 0.035% |
3. Physical Properties
| Property | SAE 1015 Carbon Steel | SAE 1006 Carbon Steel |
|---|---|---|
| Density · TYPICALUnit: g/cm³ | 7.87 g/cm³ | 7.87 g/cm³ |
| Elastic Modulus · TYPICALUnit: GPa | 205 GPa | 205 GPa |
| Poisson's Ratio · TYPICALUnit: dimensionless | 0.29 dimensionless | 0.29 dimensionless |
4. Contextual Mechanical PropertiesUnit: SI
| Mechanical Parameter | SAE 1015 Carbon SteelCold Drawn Bar (19 to 32 mm) | SAE 1006 Carbon SteelCold Drawn Bar (19 to 32 mm) |
|---|---|---|
| Ultimate Tensile Strength · Bar · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: MPa | ≥ 390 MPa | ≥ 330 MPa |
| Yield Strength · Bar · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: MPa | ≥ 325 MPa | ≥ 280 MPa |
| Elongation at Break · Bar · in 50 mm (2 in) · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: % | ≥ 18 % | ≥ 20 % |
| Reduction of Area · Bar · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: % | ≥ 40 % | ≥ 45 % |
5. Electrical & Thermal Conductive Properties
| Property | SAE 1015 Carbon Steel | SAE 1006 Carbon Steel |
|---|---|---|
| Specific Heat Capacity · TYPICALCategory: THERMAL • Unit: J/(kg·K) | 486 J/(kg·K) | 486 J/(kg·K) |
| Thermal Conductivity · TYPICALCategory: THERMAL • Unit: W/(m·K) | 51.9 W/(m·K) | 51.9 W/(m·K) |
6. Hardness Evaluation (Discrete Scales Preserved)No cross-scale mathematical conversion
| Hardness Scale | SAE 1015 Carbon Steel | SAE 1006 Carbon Steel |
|---|---|---|
| HB Hardness · Bar · Cold Drawn Bar (19 to 32 mm) · TYPICAL | ≤ 131 HB | ≤ 111 HB |