Material Comparison
Compare verified engineering materials side by side with condition-specific mechanical properties.
Material A (Baseline)
Material B (Comparison)
!
Temper & Metallurgical Context Qualification:The selected records contain different or missing source contexts. Values shown in separate rows are not directly matched. Typical and estimated values are not guaranteed minima; matching context alone does not establish interchangeability.
1. Identity, Classification & Standards
| Parameter | SAE 1044 Carbon Steel | SAE 1040 Carbon Steel |
|---|---|---|
| Material Family | Steel | Steel |
| Subfamily | Carbon Steel | Carbon Steel |
| SAE Designation | 1044 | 1040 |
| AISI Designation | 1044 | 1040 |
| UNS Designation | G10440 | — |
| SPECIFICATION Designation | SAE 1044 Carbon Steel Engineering Datasheet | SAE 1040 Carbon Steel Engineering Datasheet |
2. Chemical Composition Limits (wt %)Source-specific limits and typical values
| Element | SAE 1044 Carbon Steel | SAE 1040 Carbon Steel |
|---|---|---|
| Fe (Iron) | Bal. | — |
| C (Carbon) | 0.43 – 0.5% | 0.37 – 0.44% |
| Mn (Manganese) | 0.3 – 0.6% | 0.6 – 0.9% |
| P (Phosphorus) | ≤ 0.03% | ≤ 0.04% |
| S (Sulfur) | ≤ 0.035% | ≤ 0.05% |
3. Physical Properties
| Property | SAE 1044 Carbon Steel | SAE 1040 Carbon Steel |
|---|---|---|
| Density · TYPICALUnit: g/cm³ | 7.85 g/cm³ | 7.85 g/cm³ |
| Elastic Modulus · TYPICALUnit: GPa | 205 GPa | 205 GPa |
| Poisson's Ratio · TYPICALUnit: dimensionless | 0.29 dimensionless | 0.29 dimensionless |
4. Contextual Mechanical PropertiesUnit: SI
| Mechanical Parameter | SAE 1044 Carbon SteelCold Drawn Bar (19 to 32 mm) | SAE 1040 Carbon SteelHot rolled (estimated minimum) |
|---|---|---|
| Ultimate Tensile Strength · Bar · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: MPa | ≥ 620 MPa | — MPa |
| Tensile Strength · Bar · Hot rolled (estimated minimum) · MINIMUMUnit: MPa | — MPa | ≥ 524 MPa |
| Yield Strength · Bar · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: MPa | ≥ 515 MPa | — MPa |
| Yield Strength · Bar · Hot rolled (estimated minimum) · MINIMUMUnit: MPa | — MPa | ≥ 289.6 MPa |
| Elongation at Break · Bar · in 50 mm (2 in) · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: % | ≥ 12 % | — % |
| Elongation · Bar · Hot rolled (estimated minimum) · MINIMUMUnit: % | — % | ≥ 18 % |
| Reduction of Area · Bar · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: % | ≥ 35 % | — % |
| Reduction Of Area · Bar · Hot rolled (estimated minimum) · MINIMUMUnit: % | — % | ≥ 40 % |
5. Electrical & Thermal Conductive Properties
| Property | SAE 1044 Carbon Steel | SAE 1040 Carbon Steel |
|---|---|---|
| Specific Heat Capacity · TYPICALCategory: THERMAL • Unit: J/(kg·K) | 486 J/(kg·K) | 486 J/(kg·K) |
| Thermal Conductivity · TYPICALCategory: THERMAL • Unit: W/(m·K) | 49.8 W/(m·K) | — W/(m·K) |
| Thermal Conductivity · TYPICAL · 100 °CCategory: THERMAL • Unit: W/(m·K) | — W/(m·K) | 50 W/(m·K) |
| Coefficient of Thermal Expansion · TYPICAL · 100 °CCategory: THERMAL • Unit: µm/(m·K) | — µm/(m·K) | 11.5 µm/(m·K) |
6. Hardness Evaluation (Discrete Scales Preserved)No cross-scale mathematical conversion
| Hardness Scale | SAE 1044 Carbon Steel | SAE 1040 Carbon Steel |
|---|---|---|
| HB Hardness · Bar · Cold Drawn Bar (19 to 32 mm) · TYPICAL | ≤ 217 HB | — |
| HB Hardness · Bar · Hot rolled (estimated minimum) · MINIMUM | — | ≥ 149 HB |