1. Identity, Classification & Standards
| Parameter | SAE 1084 Carbon Steel | SAE 1065 Carbon Steel |
|---|---|---|
| Material Family | Steel | Steel |
| Subfamily | Carbon Steel | Carbon Steel |
| SAE Designation | 1084 | 1065 |
| AISI Designation | 1084 | 1065 |
| UNS Designation | G10840 | G10650 |
| SPECIFICATION Designation | SAE 1084 Carbon Steel Engineering Datasheet | SAE 1065 Carbon Steel Engineering Datasheet |
2. Chemical Composition Limits (wt %)Source-specific limits and typical values
| Element | SAE 1084 Carbon Steel | SAE 1065 Carbon Steel |
|---|---|---|
| Fe (Iron) | Bal. | Bal. |
| C (Carbon) | 0.8 – 0.93% | 0.6 – 0.7% |
| Mn (Manganese) | 0.6 – 0.9% | 0.6 – 0.9% |
| P (Phosphorus) | ≤ 0.03% | ≤ 0.03% |
| S (Sulfur) | ≤ 0.035% | ≤ 0.035% |
3. Physical Properties
| Property | SAE 1084 Carbon Steel | SAE 1065 Carbon Steel |
|---|---|---|
| Density · TYPICALUnit: g/cm³ | 7.85 g/cm³ | 7.85 g/cm³ |
| Elastic Modulus · TYPICALUnit: GPa | 205 GPa | 205 GPa |
| Poisson's Ratio · TYPICALUnit: dimensionless | 0.29 dimensionless | 0.29 dimensionless |
4. Contextual Mechanical PropertiesUnit: SI
| Mechanical Parameter | SAE 1084 Carbon SteelCold Drawn Bar (19 to 32 mm) | SAE 1065 Carbon SteelCold Drawn Bar (19 to 32 mm) |
|---|---|---|
| Ultimate Tensile Strength · Bar · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: MPa | ≥ 820 MPa | ≥ 730 MPa |
| Yield Strength · Bar · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: MPa | ≥ 660 MPa | ≥ 600 MPa |
| Elongation at Break · Bar · in 50 mm (2 in) · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: % | ≥ 8 % | ≥ 10 % |
| Reduction of Area · Bar · Cold Drawn Bar (19 to 32 mm) · MINIMUMUnit: % | ≥ 22 % | ≥ 28 % |
5. Electrical & Thermal Conductive Properties
| Property | SAE 1084 Carbon Steel | SAE 1065 Carbon Steel |
|---|---|---|
| Specific Heat Capacity · TYPICALCategory: THERMAL • Unit: J/(kg·K) | 486 J/(kg·K) | 486 J/(kg·K) |
| Thermal Conductivity · TYPICALCategory: THERMAL • Unit: W/(m·K) | 43.5 W/(m·K) | 43.5 W/(m·K) |
6. Hardness Evaluation (Discrete Scales Preserved)No cross-scale mathematical conversion
| Hardness Scale | SAE 1084 Carbon Steel | SAE 1065 Carbon Steel |
|---|---|---|
| HB Hardness · Bar · Cold Drawn Bar (19 to 32 mm) · TYPICAL | ≤ 277 HB | ≤ 248 HB |